Type
|
Powder-free and processed.
|
|
Material
|
100% natural rubber latex.
|
|
Design & Features
|
Ambidextrous; textured surface; beaded cuff; off white to yellow.
|
|
Storage
|
The gloves shall maintain their properties when stored in a dry condition at temperature not higher than 30°C.
|
|
Shelf-life
|
5 years from the date of manufacturing.
|
|
Type
|
Powder-free and processed.
|
|
Material
|
100% acrylonitrile-butadiene latex.
|
|
Design & Features
|
Ambidextrous; textured surface; beaded cuff; blue and white.
|
|
Storage
|
The gloves shall maintain their properties when stored in a dry condition at temperature not higher than 30°C.
|
|
Shelf-life
|
5 years from the date of manufacturing.
|
|
TECHNICAL SPECIFICATIONS
|
TYPE OF GLOVE
|
LATEX
|
NITRILE
|
|
Protein Level
|
< 50 µg/gm
|
N/A
|
|
Electrical Properties Resisitivity
(ANSI/ESD SP 15-01-2005) |
1 x1012 ohms/square at 50% - 60% relative humidity
|
1 x1012 ohms/square at 50% - 60% relative humidity
|
|
Total Non-volatile Residue
|
N/A
|
< 2.5 µg/cm2 (IEST-RPCC005)
|
|
Particles level (particles/cm2 )
Particles Sizes ≥ 0.5µm |
<1,500 ( IEST-RPCC005 )
|
<1,500 ( IEST-RPCC005 )
|
|
FT-IR Analysis
|
||
|
Silicone
|
None
|
None
|
|
Amide
|
None
|
None
|
|
Phatalates
|
None
|
None
|
|
Extractable Contents (Ionic)
|
||
|
Fluoride ( F- )
|
< 0.030 µg/cm2
|
< 0.005 µg/cm2
|
|
Chloride ( Cl- )
|
< 2.000 µg/cm2
|
< 0.100 µg/cm2
|
|
Bromide ( Br- )
|
< 0.030 µg/cm2
|
< 0.005 µg/cm2
|
|
Nitrate ( NO3 - )
|
< 1.000 µg/cm2
|
< 0.100 µg/cm2
|
|
Phosphate ( PO43-)
|
< 0.030 µg/cm2
|
< 0.005 µg/cm2
|
|
Sulfate ( SO42- )
|
< 1.000 µg/cm2
|
< 0.050 µg/cm2
|
|
Lithium ( Li+ )
|
< 0.002 µg/cm2
|
< 0.001 µg/cm2
|
|
Sodium ( Na+)
|
< 0.150 µg/cm2
|
< 0.050 µg/cm2
|
|
Ammonium ( NH4+ )
|
< 0.150 µg/cm2
|
< 0.050 µg/cm2
|
|
Potassium ( K+ )
|
< 0.100 µg/cm2
|
< 0.050 µg/cm2
|
|
Magnesium ( Mg2+)
|
< 0.010 µg/cm2
|
< 0.005 µg/cm2
|
|
Calcium ( Ca2+)
|
< 0.200 µg/cm2
|
< 0.050 µg/cm2
|
|
Property
|
ASTM D3578
|
ASTM D6319
|
| Elongation at break (%)
Before Aging After Aging |
min 650
min 500 |
min 500
min 400 |
| Tensile Strength(MPa)
Before Aging After Aging |
min 18
min 14 |
min 14
min 14 |
| Force at break (N)
Before Aging After Aging |
N/A
|
N/A
|